253MA STAINLESS STEEL PDF

MA® is a trademark owned by Outokumpu. Stainless AB. The standard grade designation covering this grade is UNS S Other mills produce grades. Stainless Steel MA Plate Forms of MA Available at Mega Mex. Plate; Welding Material: Bare Weld Wire, Coated Electrode and Spooled Weld Wire. With the addition of rare earth elements, RA MA still performs well at temperatures up to °F (°C), similar to that of stainless steel.

Author: Vudal Vit
Country: Iraq
Language: English (Spanish)
Genre: Music
Published (Last): 4 October 2014
Pages: 470
PDF File Size: 2.45 Mb
ePub File Size: 20.10 Mb
ISBN: 630-9-78869-482-6
Downloads: 47404
Price: Free* [*Free Regsitration Required]
Uploader: Dogami

Stainless steel MA is readily fabricated by standard commercial procedures. A wide variety of components requiring high strength at elevated temperatures such as heat exchangers, kilns, stack dampers and oven components are common applications for MA. Alloy Chemistry Data: Applications Applications include a wide variety of components requiring high strength at elevated temperatures.

Applications include a wide variety of components requiring high strel at elevated temperatures. Filler metal should be of similar composition for maximum weld integrity and properties. For improved creep strength at high temperature, consider Alloysand Positive feeds and slow speeds combined with abundant cutting fluid can minimize this alloys’ high tendency to work harden.

Stress relieve at F Cheld for minutes followed by air cooling. Megamex is a metal supplier for hastelloy, monel, inconel, stainless steel, carbon steel, metal fabrication, nickel alloys, and more. This alloy will not harden by thermal treatment.

TOP Related  BATTLE LEADERSHIP ADOLF VON SCHELL PDF

Hardening This alloy will not harden by thermal treatment. Similar in characteristics to other austenitic heat resisting alloys.

In comparison to carbon steel, stainless steels are tougher and tend to work harden rapidly. Among them are included radiant heating tubes, heat exchangers, heat treating oven components, kilns, expansion bellows and stack dampers.

Steel grade (UNS S – MA® – SS) in stainless steel

Full annealing is obtained by heating to Stwel Cholding for minutes followed by air cooling. It is austenitic in all conditions. Machinability Similar in characteristics to other austenitic heat resisting alloys. This alloy combines oxidation resistance up to F C with high strength, good general corrosion resistance and ease 253a fabrication.

Do not hold or soak at temperature due to problems associated with excessive grain growth. Due to its high strength, however, expect to use higher forces to counteract its tendency to spring-back. Humble, Texas fax Heat to F C and finish at F C.

RA 253 MA®

Stainless MA can be welded using conventional welding processes. Annealing Stress relieve at F Cheld for minutes followed by air cooling.

Stainless MA is a lean austenitic heat resistant alloy with high strength and outstanding oxidation resistance.

Nitrogen, carbon and a dispersion of rare earth and alkali metal oxides combine to provide creep rupture strength comparable to the nickel base alloys.

Developed as an alternative for and stainless in heat resistant applications by replacing some of the chromium and silicon with domestically available rare earth metals. Electrical Resistivity microhm-cm at 68 Deg F.

TOP Related  HFBR 2521 PDF

Principal Design Features This stqinless combines oxidation resistance up to F C with high strength, good general corrosion resistance and ease of fabrication. Forming This alloy can be readily sheared, formed and punched. Distributors will offer small quantity buys while mills will generally only sell large quantities, with delivery times anywhere from 10 to 50 weeks depending on size and form required This material is stocked primarily in Tubular Products by 3 distributors but is also available to a lesser extent in Wire Products, Bar Products, Flat Rolled Products, and Piping Components.

MA® – Stainless Steels Available From NeoNickel

This alloy can be readily sheared, formed and punched. However, with positive feeds and slow speeds combined with abundant cutting fluid this alloys tendency to work harden may be minimized. No forming should be performed in the range of F C due to low ductility. Modulus of Elasticity Tension. Preheating and post weld annealing are not required. Filler metal should be of similar composition for maximum weld integrity setel properties.